Abstract:
This paper deals with the formation of sulphides in as-cast grain-oriented electrical steel (GOES) thin strip during solidification and subsequent cooling through the (未 + 纬) field. Chemical composition of the strip was as follows, in mass %: 0.034 C, 2.81 Si, 0.06 Mn, 0.024 S, 0.20 Cr, 0.15 Cu, 0.055 Ni, 0.0011 Ti, 0.0056 N and 0.002 Al. It was found out that chemical composition of coarse sulphides, formed in the area of final solidification, was very different from the composition of fine sulphides precipitated in the two-phase region. Coarse sulphides were rich in iron. Fine complex sulphides were identified as the Cr2CuS4 phase. The effect of fine sulphides on the austenite decomposition at the end of the (未 + 纬) field was studied.
|